TENSION RESISTANCE OF LAMINATED COMPOSITE OF ALUMINUM WITH EPOXY RESIN REINFORCED BY GLASS FIBERS
|
| |
|
Summary :
|
|
THIS WORK STUDIED THE BEHAVIOR IN STRENGTH OF LAMINATED COMPOSITE OF ALUMINUM WITH EPOXY RESIN REINFORCED BY GLASS FIBERS. THE RESULTS OBTAINED SHOWING THE MECHANICAL PROPERTIES OF COMPOSITE DEVELOPMENT LIKE YOUNG MODULUS, YIELD STRENGTH AND RUPTURE STRENGTH. THE RESULTS FROM THE COMPOSITE TENSILE TEST WERE COMPARED WITH COMPOSITE GLARE 3 3/2 VALUES, DUE TO THIS MATERIAL IS SIMILAR TO COMPOSITE FABRICATED IN THIS WORK, SO THE COMPOSITE GLARE HAS POSITION FIBERS DISPERSED EQUALITY IN LONGITUDINAL AND TRANSVERSAL DIRECTION. THE SPECIFIC PROPERTIES FROM THE BOTH MATERIAL WERE CALCULATED. THE RESULTS HAVE SHOWN THAT COMPOSITE DEVELOPMENT IN THE LAB, SHOWED A TENSILE RESISTANCE LOWER THAN COMPOSITE GLARE 3 3/2. BY THE WAY, THE RESULTS HAD A SIGNIFICATIVY HIGH OF THE SPECIFIC PROPERTIES COMPOSITE PRODUCED IN THE LAB COMPARING WITH COMMERCIAL ALUMINUM USED.
KEY-WORDS. COMPOSITE, LAMINATED, TENSION, SPECIFIC PROPERTIES
|
| |
|
Author :
|
BASTIAN, FERNANDO LUIZ
MARTINS FONTES, OTAVIO HENRIQUE PAIVA
|
| |
|
Paper View :
|
|
COBEM99
| Organizing Committee | Keynotes
| Technical
Sessions | Author
| Symposia and special sessions
| Referees |
Work
Titles | Venue
|